Characterizationof individual filaments extracted from a Bi-2223/Ag tape

O. van der Meer, Xueyu Cai, Jianyi Jiang, Ron D. Parella, Yibing B. Huang, David C. Larbalestier, Bernard ten Haken, Herman H.J. ten Kate

Research output: Contribution to journalArticleAcademicpeer-review

29 Downloads (Pure)

Abstract

Previous studies suggest that there is a significant variation in both shape and physical properties from filament to filament in a multifilament superconducting Bi-2223/Ag tape. We are investigating this variation for a tape with a high critical current density (J/sub c/). For this study, we extracted all the filaments from a specially prepared high-quality tape having J/sub c/ (0 T, 77 K) = 45 kA/cm/sup 2/ with 19 disconnected filaments. By attaching current leads and voltage taps to the filaments, we are able to measure electrical properties on a scale of 200-300 /spl mu/m. The experiments show a large variation in filament properties. The conductivity of a filament at room temperature is proportional to its critical current density J/sub c/ at 77 K (self-field) and filaments with a higher transition temperature T/sub c/ do also show a higher J/sub c/. There is also a variation in the magnetic field behavior of the filaments. SEM pictures of the filaments also show large variations. The filaments from the center of the tape, which are thinner and have a larger aspect ratio (and thus a larger silver-filament interface), show better grain alignment and fewer impurities than filaments from the edges.
Original languageUndefined
Pages (from-to)2926-2929
Number of pages4
JournalIEEE transactions on applied superconductivity
Volume13
Issue number2
DOIs
Publication statusPublished - 2003

Keywords

  • METIS-212821
  • IR-40600

Cite this