TY - JOUR
T1 - Compression and fatigue performance of additively manufactured NiTi architected shape memory alloys
AU - Zwerink, Borit
AU - Biffi, Carlo Alberto
AU - Fiocchi, Jacopo
AU - Mehrpouya, Mehrshad
PY - 2025/9/1
Y1 - 2025/9/1
N2 - Additive manufacturing of architected materials—particularly lattice or porous structures—has gained significant attention in recent years due to their enhanced strength-to-weight ratios, load-bearing capabilities, and energy absorption properties. The integration of these structures with shape memory alloys offers multifunctional performance for advanced engineering applications. This study investigates the compressive fatigue behavior of NiTi lattice structures fabricated by Laser powder bed fusion. Initial quasi-static compression tests, carried out to full structural collapse, were used to define load levels for subsequent fatigue experiments. Fatigue testing was then conducted at 40 °C to induce pseudoelastic behavior, and an S–N curve was generated to characterize fatigue performance. Results showed that the NiTi lattice could sustain cyclic loading at 8 kN for an average of approximately 86 000 cycles, and around 18 000 cycles at 11 kN. Post-mortem microstructural analyses revealed martensite accumulation near fracture regions, attributed to stress-induced phase transformation.
AB - Additive manufacturing of architected materials—particularly lattice or porous structures—has gained significant attention in recent years due to their enhanced strength-to-weight ratios, load-bearing capabilities, and energy absorption properties. The integration of these structures with shape memory alloys offers multifunctional performance for advanced engineering applications. This study investigates the compressive fatigue behavior of NiTi lattice structures fabricated by Laser powder bed fusion. Initial quasi-static compression tests, carried out to full structural collapse, were used to define load levels for subsequent fatigue experiments. Fatigue testing was then conducted at 40 °C to induce pseudoelastic behavior, and an S–N curve was generated to characterize fatigue performance. Results showed that the NiTi lattice could sustain cyclic loading at 8 kN for an average of approximately 86 000 cycles, and around 18 000 cycles at 11 kN. Post-mortem microstructural analyses revealed martensite accumulation near fracture regions, attributed to stress-induced phase transformation.
KW - UT-Hybrid-D
UR - https://www.scopus.com/pages/publications/105017002840
U2 - 10.1088/1361-665X/ae0904
DO - 10.1088/1361-665X/ae0904
M3 - Article
SN - 0964-1726
VL - 34
SP - 09LT02
JO - Smart Materials and Structures
JF - Smart Materials and Structures
IS - 9
M1 - 09LT02
ER -