Engineering Transition Metal Layers for Long Lasting Anionic Redox in Layered Sodium Manganese Oxide

Oxygen-redox-based-layered cathode materials are of great importance in realizing high-energy-density sodium-ion batteries (SIBs) that can satisfy the demands of next-generation energy storage technologies. However, Mn-based-layered materials (P2-type Na-poor Na_y[A_xMn_1−x]O₂, where A = alkali ions) still suffer from poor reversibility during oxygen-redox reactions and low conductivity. In this work, the dual Li and Co replacement is investigated in P2-type-layered Na_xMnO₂. Experimentally and theoretically, it is demonstrated that the efficacy of the dual Li and Co replacement in Na_0.6[Li_0.15Co_0.15Mn_0.7]O₂ is that it improves the structural and cycling stability despite the reversible Li migration from the transition metal layer during de-/sodiation. Operando X-ray diffraction and ex situ neutron diffraction analysis prove that the material maintains a P2-type structure during the entire range of Na⁺ extraction and insertion with a small volume change of ≈4.3%. In Na_0.6[Li_0.15Co_0.15Mn_0.7]O₂, the reversible electrochemical activity of Co³⁺/Co⁴⁺, Mn³⁺/Mn⁴⁺, and O^2-/(O₂)^n- redox is identified as a reliable mechanism for the remarkable stable electrochemical performance. From a broader perspective, this study highlights a possible design roadmap for developing cathode materials with optimized cationic and anionic activities and excellent structural stabilities for SIBs.