Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films

A.P. Zhuravel; A.G. Sivakov; O.G. Turutanov; I.M. Dmitrenko; K. Joosse; G.J. Gerritsma; H. Rogalla

doi:10.1016/S0011-2275(05)80206-1

Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films

A.P. Zhuravel, A.G. Sivakov, O.G. Turutanov, I.M. Dmitrenko, K. Joosse, G.J. Gerritsma, H. Rogalla

Faculty of Science and Technology

Research output: Contribution to journal › Article › Academic › peer-review

63 Downloads (Pure)

Abstract

The voltage photoresponse of YBa2CH307_ x/SrTiO3 10 nm-tlfick films on laser irradiation is studied using the low temperature scanning laser microscopy (LTSLM) teclmique. The irradiation wavelength is 633 run. The spatial response dependencies via temperature (4-100 K), beam intensity modulation frequency (0-150 kHz) and bias current are examined. The bolometric and non-bolometric components are separated. The amplitude of the non-bolometric component at 4.2 K is about 10 times higher than that of bolometric one measured near the midpoint of the superconducting transition. The non-bolometric component is presumably associated with weak links in the film due to interdiffusion of SrTiO3 into YBCO layer. The spatial irregularity in superconducting parameters is not resolved by the LTSLM method since the spacing between weak links is appeared to be less than 1 um.

Original language	English
Pages (from-to)	875-878
Number of pages	4
Journal	Cryogenics
Volume	34
Issue number	Suppl. 1
DOIs	https://doi.org/10.1016/S0011-2275(05)80206-1
Publication status	Published - 1994
Event	15th International Cryogenic Engineering Conference, ICEC 1994 - Genoa, Italy Duration: 7 Jun 1994 → 10 Jun 1994 Conference number: 15

Access to Document

10.1016/S0011-2275(05)80206-1

Zhuravel94photoresponse
open
Final published version, 675 KB

Fingerprint Dive into the research topics of 'Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films'. Together they form a unique fingerprint.

Cite this

Zhuravel, A. P., Sivakov, A. G., Turutanov, O. G., Dmitrenko, I. M., Joosse, K., Gerritsma, G. J., & Rogalla, H. (1994). Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films. Cryogenics, 34(Suppl. 1), 875-878. https://doi.org/10.1016/S0011-2275(05)80206-1

@article{0c701aaba57b47568bcbffb5edbc4695,

title = "Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films",

abstract = "The voltage photoresponse of YBa2CH307_ x/SrTiO3 10 nm-tlfick films on laser irradiation is studied using the low temperature scanning laser microscopy (LTSLM) teclmique. The irradiation wavelength is 633 run. The spatial response dependencies via temperature (4-100 K), beam intensity modulation frequency (0-150 kHz) and bias current are examined. The bolometric and non-bolometric components are separated. The amplitude of the non-bolometric component at 4.2 K is about 10 times higher than that of bolometric one measured near the midpoint of the superconducting transition. The non-bolometric component is presumably associated with weak links in the film due to interdiffusion of SrTiO3 into YBCO layer. The spatial irregularity in superconducting parameters is not resolved by the LTSLM method since the spacing between weak links is appeared to be less than 1 um.",

author = "A.P. Zhuravel and A.G. Sivakov and O.G. Turutanov and I.M. Dmitrenko and K. Joosse and G.J. Gerritsma and H. Rogalla",

year = "1994",

doi = "10.1016/S0011-2275(05)80206-1",

language = "English",

volume = "34",

pages = "875--878",

journal = "Cryogenics",

issn = "0011-2275",

publisher = "Elsevier",

number = "Suppl. 1",

}

TY - JOUR

T1 - Photoresponse of epitaxial YBa2Cu3O7-x ultrathin films

AU - Zhuravel, A.P.

AU - Sivakov, A.G.

AU - Turutanov, O.G.

AU - Dmitrenko, I.M.

AU - Joosse, K.

AU - Gerritsma, G.J.

AU - Rogalla, H.

PY - 1994

Y1 - 1994

N2 - The voltage photoresponse of YBa2CH307_ x/SrTiO3 10 nm-tlfick films on laser irradiation is studied using the low temperature scanning laser microscopy (LTSLM) teclmique. The irradiation wavelength is 633 run. The spatial response dependencies via temperature (4-100 K), beam intensity modulation frequency (0-150 kHz) and bias current are examined. The bolometric and non-bolometric components are separated. The amplitude of the non-bolometric component at 4.2 K is about 10 times higher than that of bolometric one measured near the midpoint of the superconducting transition. The non-bolometric component is presumably associated with weak links in the film due to interdiffusion of SrTiO3 into YBCO layer. The spatial irregularity in superconducting parameters is not resolved by the LTSLM method since the spacing between weak links is appeared to be less than 1 um.

AB - The voltage photoresponse of YBa2CH307_ x/SrTiO3 10 nm-tlfick films on laser irradiation is studied using the low temperature scanning laser microscopy (LTSLM) teclmique. The irradiation wavelength is 633 run. The spatial response dependencies via temperature (4-100 K), beam intensity modulation frequency (0-150 kHz) and bias current are examined. The bolometric and non-bolometric components are separated. The amplitude of the non-bolometric component at 4.2 K is about 10 times higher than that of bolometric one measured near the midpoint of the superconducting transition. The non-bolometric component is presumably associated with weak links in the film due to interdiffusion of SrTiO3 into YBCO layer. The spatial irregularity in superconducting parameters is not resolved by the LTSLM method since the spacing between weak links is appeared to be less than 1 um.

U2 - 10.1016/S0011-2275(05)80206-1

DO - 10.1016/S0011-2275(05)80206-1

M3 - Article

VL - 34

SP - 875

EP - 878

JO - Cryogenics

JF - Cryogenics

SN - 0011-2275

IS - Suppl. 1

ER -