TY - JOUR
T1 - Selective metallization of alumina by laser
AU - Shrivastva, P.B.
AU - Boose, C.A.
AU - Kolster, B.H.
AU - Harteveld, C.
AU - Meinders, B.
PY - 1991
Y1 - 1991
N2 - Nickel has been selectively deposited on an alumina substrate without any pretreatment from a flow of a nickel acetate solution using the focused beam of an excimer laser. Nickel spots as well as nickel lines were drawn and subsequently plated with an electroless Ni-B coating. Excellent adhesion of the metallized layers was achieved, since with laser irradiation, both etching and deposition took place simultaneously.
AB - Nickel has been selectively deposited on an alumina substrate without any pretreatment from a flow of a nickel acetate solution using the focused beam of an excimer laser. Nickel spots as well as nickel lines were drawn and subsequently plated with an electroless Ni-B coating. Excellent adhesion of the metallized layers was achieved, since with laser irradiation, both etching and deposition took place simultaneously.
U2 - 10.1016/0257-8972(91)90155-P
DO - 10.1016/0257-8972(91)90155-P
M3 - Article
SN - 0257-8972
VL - 46
SP - 131
EP - 138
JO - Surface and coatings technology
JF - Surface and coatings technology
IS - 1
ER -