TY - JOUR
T1 - Sialon and Alumina Modified UV-Curable Coatings with Improved Mechanical Properties and Hydrophobicity
AU - Robakowska, Mariola
AU - Gierz, Łukasz
AU - Gojzewski, Hubert
PY - 2021/11/22
Y1 - 2021/11/22
N2 - This article describes the modification of UV-curable coatings with silicon aluminum oxynitride (Sialon) and aluminum oxide (Alu C), which improve the hydrophobicity of the coating surface and the scratch hardness. The contact angle is greater due to surface roughness being enhanced with inorganic fillers. Improved scratch resistance results from the formation of a sliding layer triggered by the diffusion of Sialon or alumina on the coating surface. One can observed an increase in the surface hydrophobicity as well as in the scratch hardness (up to 100%) when small amounts (5 wt.%) of the inorganic compounds are added. Imaging microscopies, i.e., SEM, OM, and AFM (with nanoscopic Young’s modulus determination), revealed the good distribution of both types of fillers in the studied matrix.
AB - This article describes the modification of UV-curable coatings with silicon aluminum oxynitride (Sialon) and aluminum oxide (Alu C), which improve the hydrophobicity of the coating surface and the scratch hardness. The contact angle is greater due to surface roughness being enhanced with inorganic fillers. Improved scratch resistance results from the formation of a sliding layer triggered by the diffusion of Sialon or alumina on the coating surface. One can observed an increase in the surface hydrophobicity as well as in the scratch hardness (up to 100%) when small amounts (5 wt.%) of the inorganic compounds are added. Imaging microscopies, i.e., SEM, OM, and AFM (with nanoscopic Young’s modulus determination), revealed the good distribution of both types of fillers in the studied matrix.
U2 - 10.3390/coatings11111424
DO - 10.3390/coatings11111424
M3 - Article
SN - 2079-6412
VL - 11
JO - Coatings
JF - Coatings
IS - 11
M1 - 1424
ER -